Polyethylene Wear With Ceramic and Metal Femoral Heads at 5 Years: A Randomized Controlled Trial With Radiostereometric Analysis
Bergvinsson, Halldor et al.Hip
Background
A common bearing combination in total hip arthroplasty today is a metal femoral head articulating with polyethylene in the cup. Ceramic heads are thought to be more resistant to third-body damage, and have better wettability and decreased surface roughness, which taken together have been suggested to result in less polyethylene wear. The purpose of this study is to compare the initial creep deformation and follow wear pattern, using radiostereometric analysis, of ceramic and metal femoral heads that articulate with a modern highly cross-linked polyethylene cup liner.
Methods
Fifty patients with primary osteoarthritis and scheduled for an uncemented total hip arthroplasty were randomized 1:1 to either a ceramic (BIOLOX delta) or a metal (CoCr) femoral head. The patients were followed up for 5 years with repeated radiostereometric analysis examinations (postoperatively, then at 14 days, 3, 12, 24, and 60 months), as well as a hip-specific outcome questionnaire.
Results
During the first 3 months both groups showed expected creep within the liner of 0.12 mm (standard deviation 0.03) for the ceramic and 0.08 mm (standard deviation 0.02) for the metal heads. Between 3 months and 5 years there was very little wear of the liner in either group, corresponding to 0.003 mm/y for ceramic and 0.007 mm/y for metal heads. There was no difference in cup migration or clinical outcome between the groups and no cups were revised.
Conclusion
With the introduction of modern highly cross-linked polyethylene, the ceramic head demonstrates no superiority when it comes to either early deformation or polyethylene wear compared with the metal head.