The Knee, ISSN: 1873-5800, Vol: 20, Issue: 3, Page: 186-90
Knee
Link to article
https://www.thekneejournal.com/article/S0968-0160(12)00152-4/fulltext
S. A.W. Van de Groes; M. C. De Waal Malefijt; N. VerdonschotKnee
Introduction
Recent clinical studies show an increased risk of femoral loosening in high-flexion TKA. Loosening seems to occur behind the anterior flange, which is covering both cancellous bone and cortical bone. It is important to optimize the interface strength between cement and both bone types to increase femoral component fixation. This study was performed to determine the cement–cortical bone interface strength for different preparation techniques.
Material and methods
A pure tensile and shear force was applied to interface specimens. The cortical surface area was prepared in three different ways: (1) Unprepared cortical bone with periosteum; (2) Periosteum removed and cortical bone roughened with a rasp; (3) Periosteum removed and three Ø3.2 mm holes drilled through the cortex. A reference group was added with a cancellous bone surface.
Results
The interface tensile strength of Group 1 was 0.06 MPa and the shear strength was 0.05 MPa. For Group 2, respectively 0.22 MPa and 1.12 MPa. For Group 3, respectively 1.15 MPa and 1.77 MPa. For cancellous bone a tensile strength of 1.79 MPa and a shear strength of 3.85 MPa were measured.
Conclusion
The strength of the cement–cancellous bone interface is superior to the cement–cortical bone interface. The preferred preparation technique of the cortical bone is to remove all the periosteum and drill holes through the cortex within the footprint of the anterior flange, to prevent cortical weakening.
Clinical relevance
Ultimately, the proposed preparation technique will lead to longer implant survival, particularly for prostheses which are used in the high-flexion range.