Clinical significance of corrosion of cemented femoral stems in metal-on-metal hips: a retrieval study
Hothi, H.S., Berber, R., Panagiotopoulos, A.C. et al.Hip
Purpose
The clinical significance of corrosion of cemented femoral stems is unclear. The purpose of this retrieval study was to: (1) report on corrosion at the stem-cement interface and (2) correlate these findings with clinical data.
Methods
We analysed cemented stems (n = 36) composed of cobalt-chromium (CoCr) and stainless steel (SS) in a series of revised metal-on-metal hips. We performed detailed inspection of each stem to assess the severity of corrosion at the stem-cement interface using a scale of 1 (low) to 5 (severe). We assessed the severity of corrosion at each stem trunnion and measured wear rates at the head taper and bearing surfaces. We used non-parametric tests to determine the significance of differences between the CoCr and SS stems in relation to: (1) pre-revision whole blood Co and Cr metal ion levels, (2) trunnion corrosion, (3) bearing surface wear and (4) taper material loss.
Results
The corrosion scores of CoCr stems were significantly greater than SS stems (p < 0.01). Virtually all stem trunnions in both alloy groups had minimal evidence of corrosion. The median pre-revision Co levels of implants with CoCr stems were significantly greater than the SS stems (p < 0.01). There was no significant difference in relation to pre-revision Cr levels (p = 0.521). There was no significant difference between the two stem types in relation to bearing wear (p = 0.926) or taper wear (p = 0.148).
Conclusions
Severe corrosion of cemented femoral stems is a common finding at our retrieval centre; surgeons should consider corrosion of CoCr stems as a potential source of metal ions when revising a hip.
Link to article