Mechanical characteristics of the bone–graft–cement interface after impaction allografting

Impaction allografting is an attractive procedure for the treatment of failed total hip replacements. The graft–cement–host bone interface after impaction allografting has not been characterized, although it is a potential site of subsidence for this type of revision total hip reconstruction. In six human cadaveric femurs, the cancellous bone was removed proximally and local diaphyseal lytic defects were simulated. After the impaction grafting procedure, the specimens were sectioned in 6 mm transverse sections and pushout tests were performed. From the adjacent sections the percentage cement contact of the PMMA cement with the endosteal bone surface was determined. The host bone interface mechanical properties varied significantly along the femur largely due to different interface morphologies. The apparent host bone interface shear strength was highest around the lesser trochanter and lowest around the tip of the stem. A significant positive correlation was found between the percentage cement contact and the apparent host bone interface shear strength (r² = 0.52). The sections failed in 69% of the cases through a pure host bone interface failure without cement or allograft failure, 19% failed with local cement failure, and 12% with a local allograft failure. The apparent host bone interface strength was on average 89% lower than values reported for primary total hip replacements and were similar to cemented revisions proximally and lower distally. This study showed that cement penetration to the endosteal surface enhanced the host bone–graft interface.