Incidence, Risk Factors, and Outcome of Ceramic-On-Ceramic Bearing Breakage in Total Hip Arthroplasty

Ceramic-on-ceramic bearing breakage is a rare but significant complication of total hip arthroplasty. This study aimed to identify risk factors for breakage and to determine the outcome of different revision options.

All ceramic-on-ceramic primary total hip arthroplasty procedures reported to the Australian Joint Replacement Registry from September 1999 to December 2019 were included. Procedures were subdivided into alumina or mixed ceramic (alumina/zirconia). All breakages were identified. The association between ceramic type and head size was assessed. Subsequent revision rates were compared and cause of revision assessed.

There were 23,534 alumina and 71,144 mixed ceramic procedures. Breakage was the reason for 1^st revision in 84 alumina (5.27% of all revisions and 0.36% of procedures) and 56 mixed ceramic procedures (2.46% of all revisions; 0.08% of procedures). Alumina had a higher breakage rate than mixed ceramic (HR 2.50 (95% CI 1.75, 3.59), P < .001), and breakage was higher for 36-38mm head sizes using alumina (HR 2.84 (1.52, 5.31), P = .001). 17.8% of 2^nd revisions occur by 3 years, due to dislocation, infection, metal-related pathology, and loosening. A neck adapter sleeve did not reduce 2^nd revisions. Numbers were too low to compare revision bearing surface options.

Ceramic breakage has reduced with mixed ceramics but has a 0.79/1000 incidence at 15-year follow-up. It is unclear what the risk factors are for modern ceramics with increasing head size a risk for alumina only. Risk of 2^nd revision is high and occurs early. The optimal revision option is unknown.